- Overview
- Application
Basic Info.
Model NO.
Conveyor Belt
Feature
Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant
Tensile Strength
Strong
Type of Belt
Ep/Nn/ Steel Cord/Sold Woven/Sidewall/Rough Top
Grade of Belt DIN
DIN-Z-15MPa. 18MPa. 20MPa .24MPa
Grade of Belt Rma
Rma-I 17MPa, Rmaii-14MPa
Grade of Belt as
As1332-a 17MPa, M24MPa
Grade of Belt ISO
ISO-H BS490-M24MPa
Grade of Belt JIS
JIS6332-G 14MPa. D-18MPa
Grade of Belt SABS
SABS-M
Grade of En14973
En14973 C1, C2, A1, B1, B2
Heat Resistant of Belt
T1:100-120/T3:Hr150/T4:Hr180
Flame Retardant Conveyor Belt
DIN-K, Mt668/Mt914/ISO15326-K
Transport Package
PP Package/ Iron Shelf/Iron Pallet/Wooden Pallet/W
Trademark
ZHENXING
Origin
China
HS Code
40101200
Production Capacity
200000000sqm/Year
Packaging & Delivery
Package Size
160.00cm * 100.00cm * 160.00cm
Package Gross Weight
5000.000kg
Product Description
FABRIC RUBBER CONVEYOR BELTS
ZHENXING conveyor belts are quality products with an extremely high degree of reliability and are the
qualified manufacturer of different types of conveyor belts meeting all the requirements in most industrial activities.
Conveyor Belt Construction
Top Cover
Designed to protect the carcass from service conditions like oil,heat, abrasion, etc.
Skim Coat
Compounded for excellent adhesion between plies for protecting against ply separation.
Carcass
Extremely low stretch characteristics of fabric and good troughability.
Bottom Cover
Excellent in abrasion and fexibility, provides wearing surface against pulleys and idlers.
Designed to protect the carcass from service conditions like oil,heat, abrasion, etc.
Skim Coat
Compounded for excellent adhesion between plies for protecting against ply separation.
Carcass
Extremely low stretch characteristics of fabric and good troughability.
Bottom Cover
Excellent in abrasion and fexibility, provides wearing surface against pulleys and idlers.
COVER RUBBER THICKNESS
| Condition Material Carried Lump Size Belt Cycle (Second) 0~20 20~60 60~300 | Moderately Abrasive | Abrasive | Very Abrasive | Extremely Abrasive | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Fine Coal, Grain, Wood Chips, Ash, Cement, etc. 0 ~ 2″ (0~50mm) 1/16 ~ 1/8 (1.5~3.0mm) 1/16 ~ 3/32 (1.5~2.5mm) 1/16 ~ 1/32 (1.5~0.8mm) | Sand, Coal, Clay, Salt, etc. 2″ ~ 6″ (50~150mm) 1/8 ~ 3/16 (3.0~5.0mm) 1/8 ~ 3/16 (3.0~5.0mm) 1/16 ~ 3/32 (1.5~2.5mm) | Limestone, Crushed Stone, Coke, etc. 6″ ~ 10″ (150~250mm) 3/16 ~ 1/4 (5.0~6.0mm) 3/16 ~ 1/4 (5.0~6.0mm) 1/8 ~ 3/16 (3.0~5.0mm) | Ores, Slag, Cullet, etc. 8″~ 12″ (200~300mm) 1/4 ~ 5/16 (6.0~8.0mm) 1/4 ~ 5/16 (6.0~8.0mm) 3/16 ~ 1/4 (5.0~6.0mm) | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Cover Grade | Tensile Strength Min.(Mpa) | Elongation Min.(%) | Abrasion Loss Max.(mm³) | |||||||||||||||||||||||||||||||||||||||||||||||
| DIN - X | 25 | 450 | 120 | |||||||||||||||||||||||||||||||||||||||||||||||
| DIN - W | 18 | 400 | 90 | |||||||||||||||||||||||||||||||||||||||||||||||
| AS - A | 17 | 400 | 70 | |||||||||||||||||||||||||||||||||||||||||||||||
Note: Abrasion test is based on DIN 53516
POLYESTER FABRIC (EP) CONVEYOR BELT
The combination of polyester in warp and nylon in filling provides technically low-stretch and high impact
abuse resistance.
• Special Features
• High resistance to tension.
• Low elongation.
• Outstanding stability dimensionally.
• Impact resistance.
• Complete moisture & mildew protection
| General Conveyor Belt This Construction, utilizing all nylon, offers maximum impact and damage resistance from material and suitable for transporting a variety of materials(ore, crushed stones, grain, sand, etc.). Several types of carcass using NN/EP fabrics with various thickness are available according to the load conditions. |
| Grade | EP100 | EP125 | EP150 EP200 | EP250 | EP300 | EP350 | EP400 | EP500 | |||||||||||||||||||||||||||||||||||||||||||||||||||
| Min. Tensile Strength | kg/cm-ply lb/in-ply | 100 | 125 | 150 | 200 | 250 | 300 | 350 | 400 | 500 | |||||||||||||||||||||||||||||||||||||||||||||||||
| 560 | 700 | 850 | 1,120 | 1,400 | 1,680 | 2,000 | 2,240 | 2,800 | |||||||||||||||||||||||||||||||||||||||||||||||||||
| Working Tension Rating (Vulcanized) | kg/cm-ply lb/in-ply | 10.0 56.0 | 12.5 70.0 | 15.0 84.0 | 20.0 112.0 | 25.0 140.0 | 30.0 168.0 | 35.0 200.0 | 40.0 224.0 | 50.0 280.0 | |||||||||||||||||||||||||||||||||||||||||||||||||
| Approx. Gauge per Ply | mm | 0.9 | 1.2 | 1.4 | 1.5 | 1.9 | 2.0 | 2.1 | 2.4 | 3.2 | |||||||||||||||||||||||||||||||||||||||||||||||||
| with skim coat. | inch | 0.035 | 0.047 | 0.055 | 0.059 | 0.075 | 0.079 | 0.083 | 0.094 | 0.126 | |||||||||||||||||||||||||||||||||||||||||||||||||
NYLON FABRIC (NN) CONVEYOR BELT
Special Features
• Exceptionally shock & impact resistance to the carrying surface.
• Superior in fastener holding ability.
• Excellent troughability and flexibility
• Smaller pulley available.
• Greatest resistance to water and mildew.
Special Features
• Exceptionally shock & impact resistance to the carrying surface.
• Superior in fastener holding ability.
• Excellent troughability and flexibility
• Smaller pulley available.
• Greatest resistance to water and mildew.
| Grade | NN100 | NN120 | NN150 | NN200 | NN250 | NN300 | NN350 | NN400 | NN500 | ||||||||||||||||||||||||||||||||||||||||||||||||||
| Min. Tensile Strength | kg/cm-ply lb/in-ply | 100 | 120 | 150 | 200 | 250 | 300 | 350 | 400 | 500 | |||||||||||||||||||||||||||||||||||||||||||||||||
| 560 | 672 | 840 | 1,120 | 1,400 | 1,680 | 1,960 | 2,240 | 2,800 | |||||||||||||||||||||||||||||||||||||||||||||||||||
| Working Tension Rating (Vulcanized) | kg/cm-ply lb/in-ply | 8.4 46.7 | 10.0 56.0 | 12.5 70.0 | 16.7 93.3 | 20.8 116.7 | 25.0 140.0 | 29.2 163.3 | 33.3 186.7 | 41.7 233.3 | |||||||||||||||||||||||||||||||||||||||||||||||||
| Approx. Gauge per Ply | mm | 0.9 | 1.2 | 1.3 | 1.5 | 1.6 | 1.8 | 2.0 | 2.2 | 2.7 | |||||||||||||||||||||||||||||||||||||||||||||||||
| with skim coat. | inch | 0.035 | 0.047 | 0.051 | 0.059 | 0.063 | 0.071 | 0.079 | 0.087 | 0.106 | |||||||||||||||||||||||||||||||||||||||||||||||||
| Grade | 160 | 200 | 250 | 315 | 400 | 500 | 630 | 800 | 1000 | 1250 | 1600 | 2000 | |||||||||||||||||||||||||||||||||||||||||||||||
| 2ply 3ply 4ply 5ply 6ply | 160/2 | 200/2 | 250/2 250/3 | 315/2 315/3 | 400/2 400/3 400/4 | 500/3 500/4 500/5 | 630/3 630/4 630/5 630/6 | 800/3 800/4 800/5 800/6 | 1000/3 1000/4 1000/5 1000/6 | 1250/3 1250/4 1250/5 1250/6 | 1600/4 1600/5 1600/6 | 2000/5 2000/6 | |||||||||||||||||||||||||||||||||||||||||||||||
| Flame Resistant Conveyor Belt Lorbrand Flame resistant conveyor belt is designed for the best service conditions of coal mining industries. It is suitable for mining, power plant, electric utilities, coal cleaning plants. The different rubber compounds are available in accordance with its requirement. |
1.FR-MOR
Grade is fire resistance with medium oil resistance and accepted by USMSHA(Mine Safety and Health Administration).
It is recommended for the typical applications like oil treated coal and grain industries requiring fire & oil resistance, and static conductivity with lower electric resistance than 1MΩ .
Grade is fire resistance with medium oil resistance and accepted by USMSHA(Mine Safety and Health Administration).
It is recommended for the typical applications like oil treated coal and grain industries requiring fire & oil resistance, and static conductivity with lower electric resistance than 1MΩ .
2.FR-SBR
Grade is SBR fire resistant cover rubber meeting USMSHA (Mine Safety and Health Administration). It provides highly resistanceto wear and cold resistance.
Grade is SBR fire resistant cover rubber meeting USMSHA (Mine Safety and Health Administration). It provides highly resistanceto wear and cold resistance.
3.FR-GR
Grade is specially compounded SBR cover
rubber for the under-ground operation
requiring fire resistance, static conductivity.
The important characteristic is self
extinguishable cover rubber.
Grade is specially compounded SBR cover
rubber for the under-ground operation
requiring fire resistance, static conductivity.
The important characteristic is self
extinguishable cover rubber.
• Flame Resistant
Cover Rubber Grade: USMSHA, SABS, DIN, AS, etc.
| Type | Cover Rubber | ||||||||||||||||||||||||||||||
| Application Grade | Min. Tensile kg/cm² psi | Min. Elongation (%) | |||||||||||||||||||||||||||||
| FR-MOR | MSHA/MOR(USA) | 150 | 2100 | 400 | |||||||||||||||||||||||||||
| FR-SBR | MSHA/SBR(USA) | 140 | 2000 | 400 | |||||||||||||||||||||||||||
| FR-GR | ISO, DIN, JIS, KS | 140 | 2000 | 400 | |||||||||||||||||||||||||||
Certiied USA • FR-MOR(MSHA/MOR/SC) USMSHA No. 28-85/6
• FR-SBR(MSHA/SBR) USMSHA No. 28-85/5
RUSSIA • FR-MOR POCC KR BO1408
• FR-SBR POCC KR BO1324
| Heat Resistant Conveyor Belt The performance-proved Lorbrand Belt : Heat resistant belt meets hot service application like hot sintered ore, hot pellet, hot clinker, hot chemical, fertilizer, hot cement. |
SPECIAL FEATURES
• Excellent heat resistant and abrasion resistant cover rubber compound.
• Recommended to protect belt from surface cracking and hardening by heat.
• Specially heat-treated and dipped fabric to minimize carcass shrinkage by heat
aging.
HT-710 & SUPER-HT Exwill conveyor belt are the best selection for wide ranges of high temperature application.
Heat resistant conveyor belts are most suitable for heat resistant applications where the temperature of material to be carried is over 60°C(140°F).
• Excellent heat resistant and abrasion resistant cover rubber compound.
• Recommended to protect belt from surface cracking and hardening by heat.
• Specially heat-treated and dipped fabric to minimize carcass shrinkage by heat
aging.
HT-710 & SUPER-HT Exwill conveyor belt are the best selection for wide ranges of high temperature application.
Heat resistant conveyor belts are most suitable for heat resistant applications where the temperature of material to be carried is over 60°C(140°F).
| Temperature | Type | Compound of Cover Rubber | Temperature Range of Use | Application | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Belt Surface Temp | Average Material Temp | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Max.°F | Max.°C | Max.°F | Max.°C | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Medium Temperature High Temperature High Temperature Extremely High Temperature | HT-400 (HR-100) ECO-HT HT-710 (HR-150) SUPER-HT (HR-200) | SBR EPM/SBR EPM EPM | 210°F 270°F (300°F) Max. 300°F Max. 400°F | 100°C 130°C (150°C) 150°C 200°C | Lump 300°F Fines 250°F Lump 550(650)°F Fines 300(400)°F Lump 650°F Fines 100°F Lump 750°F Fines 480°F | Lump 150°C Fines 120°C Lump 300(350)°C Fines 150(200)°C Lump 350°C Fines 200°C Lump 400°C Fines 250°C | For low temperature with abrasive material. (coke, sintered products, etc.) For higher temperature use with lower temperature condition on bottom cover than HT-710 Top cover: EPM, Bottom cover: SBR - Economical version of HT-710 (dried clay, cement clinker, etc.) For higher temperature use. (dried clay, cement clinker, etc.) For extremely high temperature application. (sintered ore, cement clinker, chemicals, etc.) | |||||||||||||||||||||||||||||||||||||||||||||||||||||
| Materials Carried | Lump Size | Temperature of Material Carried | Belt Surface Temperature | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Sintered Ore Return of Sintered Ore Coke Raw Material Clinker Cement Metal Powder Molding Sand | 25~200 mm(1~8 inch) 10 mm(0.4 inch) downward 100~200 mm(4~8 inch) 30 mm(1.2 inch) downward 10~30mm(0.4~1.2 inch) Powder - - | 200~400°C(390~750°F) 260°C(480°F) 70~100°C(160~210°F) 180~220°C(360~410°F) 100~220°C(210~410°F) 100~125°C(210~250°F) 170°C(340°F) 200~250°C(390~480°F) | 130~150°C(270~300°F) 150~190°C(300~370°F) 50~60°C(120~140°F) 100~120°C(210~250°F) 100~110°C(210~230°F) 80~90°C(170~190°F) 120~130°C(250~270°F) 80~90°C(170~190°F) | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| HEAT RESISTANT CONVEYOR BELT (CTND) USER OF ATTENTION The temperature of material being transported and the belt's surface temperature vary according to the material and shape. For instance, when materials have a temperature of 150ºC(300ºF) (such as coke or sintered ore) and have a relatively small contact area, Lorbrand conveyor belt's surface temperature could remain at 60~80ºC(140~180ºF). In contrast, when powdered material like cement is being conveyed, the material temperature and the belt surface temperature do not differ so greatly. The lifetime of heat resistant belt is largely affected by the belt's surface temperature during operation. |
CHARACTERISTICS INDISPENSABLY REQUIRED FOR HEAT RESISTANT LORBRAND
CONVEYOR BELT ARE AS FOLLOWS:
• Rubber cover and carcass should not deteriorate due to heat.
• Rubber cover and carcass should maintain excellent properties, even at high temperatures and good adhesion to form one unit, even when they are exposed to high temperatures.
The surface temperature of heat resistant Lorbrand conveyor belt varies with the material type, belt speed,loading rate and size depending on circumstance condition. In order to select the proper heat resistant Lorbrand conveyor belt, it is necessary to consider not only the material temperature to be conveyed but also the surface temperature of Lorbrand conveyor belt.
CONVEYOR BELT ARE AS FOLLOWS:
• Rubber cover and carcass should not deteriorate due to heat.
• Rubber cover and carcass should maintain excellent properties, even at high temperatures and good adhesion to form one unit, even when they are exposed to high temperatures.
The surface temperature of heat resistant Lorbrand conveyor belt varies with the material type, belt speed,loading rate and size depending on circumstance condition. In order to select the proper heat resistant Lorbrand conveyor belt, it is necessary to consider not only the material temperature to be conveyed but also the surface temperature of Lorbrand conveyor belt.
| Materials Carried | Temperature of Materials Carried | Belt Surface Temperature | Heat Resistant Conveyor Belt Grade | ||||||||||||||||||||||||||||||||||||||
| 200°C downward 50~100°C | HT-400 | ||||||||||||||||||||||||||||||||||||||||
Sintered Ore | 100°C downward (Lump Condition) 200°C upward 100~130°C 130~180°C | HT-400 | |||||||||||||||||||||||||||||||||||||||
| HT-550 (Lump Condition) HT-710 HT-710, HT-850 | |||||||||||||||||||||||||||||||||||||||||
| Return of Sintered Ore | 150°C downward 150°C upward | 50~80°C 80°C downward (Lump Condition) 80~130°C 130~180°C | HT-400 HT-400 HT-550 HT-710, HT-850 | ||||||||||||||||||||||||||||||||||||||
| Spherical Ore | 120°C upward 80°C downward | HT-400 | |||||||||||||||||||||||||||||||||||||||
| 120°C downward 80°C upward | HT-550 | ||||||||||||||||||||||||||||||||||||||||
| Pellet | 150°C downward 200°C downward | 100°C downward | HT-400 (Lump Condition) | ||||||||||||||||||||||||||||||||||||||
| Coke | 60~400°C 100°C downward | HT-400 | |||||||||||||||||||||||||||||||||||||||
| 120°C downward 50~80°C | HT-400 (Lump Condition) | ||||||||||||||||||||||||||||||||||||||||
| Cement | 120°C upward | 80~130°C 130~180°C | HT-550 | ||||||||||||||||||||||||||||||||||||||
| HT-710 HT-710, HT-850 | |||||||||||||||||||||||||||||||||||||||||
| Dried Lime Dried Clay | 120~150°C 200°C downward | 100°C upward 50~100°C | HT-400 (Lump Condition) | ||||||||||||||||||||||||||||||||||||||
| HT-550 (Lump Condition) HT-400 | |||||||||||||||||||||||||||||||||||||||||
| 500°C upward | 100~130°C 130~180°C | HT-550 | |||||||||||||||||||||||||||||||||||||||
| HT-710, HT-850 | |||||||||||||||||||||||||||||||||||||||||
| Cement Steel Mill Chemical Fertilizers | 80°C downward 50~70°C | HT-400 | |||||||||||||||||||||||||||||||||||||||
| 80°C upward 120~180°C | HT-550 HT-710, HT-850 | ||||||||||||||||||||||||||||||||||||||||
| 120°C downward 50~100°C | HT-400 | ||||||||||||||||||||||||||||||||||||||||
Molding | 120°C upward 120~180°C | HT-550 | |||||||||||||||||||||||||||||||||||||||
| HT-710 HT-710, HT-850 | |||||||||||||||||||||||||||||||||||||||||
RESTRICTIONS ON THE USE OF HEAT-RESISTANT BELT
• SBR Heat-resistant belt
Do not use SBR heat resistant belt when :
• Powdered material is over 70ºC(160ºF)
• Strong acid or alkaline is used
• Oil products and oil-staine substances are used.
• The operation site or the materials require flame-resistant belts.
• EPR(EPM) Heat-resistant belt
Do not use EPR(EPM) heat-resistant belts when :
• Powdered material is over 180ºC(350ºF)
• Oil products and oil-stain other than vegetable oil are present.
• The location of the materials requires flame-resistant belts.
• SBR Heat-resistant belt
Do not use SBR heat resistant belt when :
• Powdered material is over 70ºC(160ºF)
• Strong acid or alkaline is used
• Oil products and oil-staine substances are used.
• The operation site or the materials require flame-resistant belts.
• EPR(EPM) Heat-resistant belt
Do not use EPR(EPM) heat-resistant belts when :
• Powdered material is over 180ºC(350ºF)
• Oil products and oil-stain other than vegetable oil are present.
• The location of the materials requires flame-resistant belts.
| Oil/Heat & Oil Resistant Conveyor Belt The cover rubber is especially compounded for the applications requiring resistance to oils. It has outstanding abrasion, ozone and weather resistance. This Lorbrand conveyor belt is recommended for the conveyor lines causing swelling and sponginess by oils. |
OR-100
Grade is to resist Moderate Oil Resistant operations like wood chips, linseed, cottonseed and whole soybeans where static conductivity is needed.
Grade is to resist Moderate Oil Resistant operations like wood chips, linseed, cottonseed and whole soybeans where static conductivity is needed.
OR-200
Grade has superior oil resistance to various kinds of animal and vegetable oil with severe cold temperature up to -45ºC (50ºF)
Grade has superior oil resistance to various kinds of animal and vegetable oil with severe cold temperature up to -45ºC (50ºF)
OR-300
Grade has excellent resistance to the toughest oil application such as oil-treated coal, petroleum based oils.
Grade has excellent resistance to the toughest oil application such as oil-treated coal, petroleum based oils.
| Type | Min. Tensile Strength kg/cm² psi | Min. Elongation (%) | Volume Change(%) ASTM #3 Oil | Use | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| OR-100 | 100 1400 | Min. 350 | Max. 150 | Wood chip, linseed, cottonseed, kernel corn, and whole soybeans, static conductivity, and moderate oil resistance. | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| OR-200 | 120 1700 | Min. 350 | Max. 90 | Oil-treated materials and for carrying oily metal turnings and shavings, crushed soybeans, animal or vegetable fats. | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| OR-300 | 120 1700 | Min. 400 | Max. 20 | Oily metal parts, crushed soybeans, automatic hydrocarbons such as benzol, toluene and petroleum based oils. | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| HTN/HOT | 120 1700 | Min. 400 | Max. 60 | Hot asphalt and other oil& heat resistant applications. | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Oil resistance (volume change) and immersion condition: 70°C × 96 Hrs.
| Incline (Chevron Cleated) Conveyor Belt------Support custom (Chevron )pattern mold. Lorbrand Incline (Chevron-Cleated) conveyor belt is used to carry sand, fine coal and grain materials by using steep inclines. Chevron Cleats increase the quantity of granular materials in Fabric incline applications. |
SPECIAL FEATURES
• High quality fabric with low stretch.
• Cleat angle and pitch are designed for smooth travel over return idlers.
• Higher angle of 17~30 degree of incline.
• Wear resistant and oil resistant black rubber quality is available.
• High quality fabric with low stretch.
• Cleat angle and pitch are designed for smooth travel over return idlers.
• Higher angle of 17~30 degree of incline.
• Wear resistant and oil resistant black rubber quality is available.
| Sidewall Conveyor Belt This Lorbrand belt is designed with two corrugated sidewalls molded to crossrigid basebelt. It is developed in order to meet larger capacities with more steep inclined line. |
| STEEL CORD RUBBER CONVEYOR BELT Lorbrand Steel Cord Rubber Conveyor Belt can be widely used in the coal industry, mines,ports, power plants and chemical industry for conveying materials.. |
Performance Of Conveyor Belts
S
| Solid Woven Conveyor Belt PVG fabric whole core flame retardant conveyor belt is designed and produced according to MT914-2019 standard. The product quality of enterprises that have passed IS09001 quality system certification has reached the international advanced level. This product is made of solid weven cavcass with chemical fiber and cotton as the skeleton, impregnated with paste, pasted with rubber covering and vulcanized. |
Solid Woven Conveyor Belt:
A. Surface resistance value: ≤ 3 × 108Ω
| Tensile strength/MPa | Elongation at break% | Abrasion/mm |
| ≥10.0 | 350% | ≤200 |
A. Surface resistance value: ≤ 3 × 108Ω
B. Drum Friction performance : the surface temperature of the drum is ≤ 325 ºC, and there is no flame
combustion or flameless combustion.
C. Combustion performance of alcohol blowtorch:
Test piece with covering layer: average value ≤ 3.0 S, single value ≤ 10.0 S
Test piece without of covering layer: average value ≤ 5.0 S, single value ≤ 15.0 S
D. Tunnel propane combustion performance: retention length of undamaged lenght > 600mm
Fensile strength | Minimum wap strength N/mm | Minimum weft strength N/mm | Minimum tear force N | Minimum elongation at break in warp direction | Min elongation at break in weft direction at break |
| 680 | 680 | 265 | 1090 | 15 | 18 |
| 800 | 800 | 280 | 1180 | 15 | 18 |
| 1000 | 1000 | 300 | 1180 | 15 | 18 |
| 1250 | 1250 | 350 | 1540 | 15 | 18 |
| 1400 | 1400 | 350 | 1540 | 15 | 18 |
| 1600 | 1600 | 400 | 15 | 18 | |
| 2000 | 680 | 400 | 15 | 18 |
| Rough Top Conveyor Belt Rough Top Conveyor Belt can be used for tilt angleLight materials such as bags, boxes and parcels are transported at 35 degrees angle. The top rubber surface is wear-resistant and skid-resistant rubber. It has the functions of cushioning, shock absorption and stabilization for material transportation, especially anti-skid. |
| Pipe Conveyor Belt Lorbrand pipe conveyor belt is designed to be suitable for the resistance to flex fatigue and abrasion by materials to be carried with superior ply adhesion. |
| Pipe Diameter (mm, ø) | Cross Section Area (75%) | Belt Speed (m/min) | Capacity (m³/hr) | Material Size (mm) | Comparison with Standard C/Belt(mm) | ||||||||||||||||||||||||||||||||||||
| 150 | 0.013 | 120 | 95 | 30~50 | 300~500 | ||||||||||||||||||||||||||||||||||||
| 200 | 0.023 | 130 | 180 | 50~70 | 500~600 | ||||||||||||||||||||||||||||||||||||
| 250 | 0.041 | 140 | 344 | 70~90 | 600~750 | ||||||||||||||||||||||||||||||||||||
| 300 | 0.049 | 145 | 441 | 90~100 | 750~900 | ||||||||||||||||||||||||||||||||||||
| 350 | 0.066 | 175 | 693 | 100~120 | 900~1,050 | ||||||||||||||||||||||||||||||||||||
| 400 | 0.108 | 200 | 1,296 | 120~150 | 1,050~1,200 | ||||||||||||||||||||||||||||||||||||
| 500 | 0.155 | 225 | 2,093 | 150~200 | 1,200~1,500 | ||||||||||||||||||||||||||||||||||||
| 600 | 0.216 | 250 | 3,240 | 200~250 | 1,500~1,800 | ||||||||||||||||||||||||||||||||||||
| 700 | 0.290 | 275 | 4,620 | 250~300 | 1,800~2,000 | ||||||||||||||||||||||||||||||||||||
| 850 | 0.404 | 300 | 7,272 | 300~400 | 2,000~2,200 | ||||||||||||||||||||||||||||||||||||
SPECIAL FEATURES
• Closed transportation in order to prevent materials from overflowing, drop-down, scattering and mixing with foreign materials from outside.
• This Lorbrand pipe conveyor belt is economical for curve (45°~90°) and incline(up to 30°) transportation due to easy design of conveyor line and limited space.